ANTI-SEIZE NICKEL PASTE
GREASE FOR EXTREME TEMPERATURES
ASSEMBLY, INSTALLATION, REMOVAL
STATIC LUBRICATION OF COMPONENTS SUBJECT TO STRONG VIBRATIONS
DYNAMIC LUBRICATION OF SLOW-MOVING PARTS
STEEL-WORKING, FOUNDRIES, FORGES
COMPLIES WITH SPECIFICATIONS
MIL A 907 ED - STM 7411 A
SECLF 216 - MIL A 907 E 80
DESCRIPTION
Very high performance anti-seize nickel paste.
The interaction between the nickel and the other loads enables the avoidance of catalytic coupling between Fe/Cu contacts; or as can be seen with copper anti-seize agents, in Fe/Fe contacts. This product can thus be used risk-free on all ferrous metals, including chrome.
Product guaranteed free of metalloids and nitrites.
Effective in dynamic use, in static use and in the presence of vibrations.
Do not use on bearings or slow-moving rollers without frequently applying lubricant.
Allows you to obtain results at very high temperatures of up to 1200°C when protection limits are in place.
Complies with MIL A 907 E/D, ST7411A and SECLF 216 specifications.
Do not use on bearings or rollers in operation without frequently applying lubricant.
FIELDS OF USE
NEOLUBE® METAL 1200 grease is used for the same applications as the METAL 900 aluminium and METAL 1100 copper greases, with a view to resolving surface oxidisation problems in the case of catalytic coupling. Pitting.
INSTRUCTIONS FOR USE
Shake the aerosol can vertically for a few moments after the ball in the can becomes detached. First degrease the mechanism to be lubricated as needed using Neutralène® V200 aerosol. Spray at a distance of 15 to 25 cm depending on the size of the mechanism.
TYPICAL PHYSICO-CHEMICAL PROPERTIES
|
PHYSICAL PROPERTIES OF THE GREASE |
|||
|
PROPERTIES |
STANDARD OR METHOD |
VALUE |
UNIT |
|
Appearance |
Visual |
Paste |
- |
|
Colour |
Visual |
Metallic grey |
- |
|
Apparent density at 25°C (pycnometer) |
NF T 30 020 |
910 |
kg/m³ |
|
NLGI Class |
NLGI National Lubricating Grease Institute |
2 |
Classification |
|
Thickener |
- |
Inorganic |
- |
|
Solid lubricant content |
- |
Nickel/aluminium |
12% |
|
Penetrability at 25°C Non-worked Worked, 60 strokes Worked, 1,000 strokes Worked, 10,000 strokes Worked, 100,000 strokes |
NF ISO 2137 / ASTM 2176
|
265-295 265-295 265-295 275-305 275-305 |
1/10° mm 1/10° mm 1/10° mm 1/10° mm 1/10° mm |
|
Dropping point Dropping point if greater than 360°C |
NF ISO 2176 / ASTM D 566 ASTM D 2265 |
190 - |
°C
|
|
Impurities > 25 µm > 75 µm > 125 µm |
FMTS 791 3005 |
nm nm nm |
nb/ml nb/ml nb/ml |
|
PHYSICO-CHEMICAL PROPERTIES OF THE BASE OIL |
|||
|
PROPERTIES |
STANDARD OR METHOD |
VALUE |
UNIT |
|
Characteristics of the base oil |
- |
Polymer |
- |
|
Kinematic viscosity at 40°C Kinematic viscosity at 100°C |
NF EN ISO 3104 |
140 100 |
mm/s־¹ mm/s־¹ |
|
Acid value (AV) |
NF ISO 6618 |
<0.38 |
mg KOH/l |
|
PERFORMANCE PROPERTIES |
|||
|
PROPERTIES |
STANDARD OR METHOD |
VALUE |
UNIT |
|
Oil separation, 7 days at 40°C (bleeding) |
NF T 60 191 |
0 |
% of mass |
|
Oil separation, 24 hours at 41 kPa (bleeding under pressure) |
ASTM D 1742 |
<3 |
% of mass |
|
Sulphated ashes |
NF T 60 144 |
1.5 |
% of mass |
|
Copper strip corrosion |
ASTM D 4048 |
1a |
Rating |
|
Hoffman oxidation |
ASTM D 942 |
<10 |
psi |
|
Loss by evaporation, 22 hours at 121°C |
ASTM D 972 |
0.1 |
% of mass |
|
Noack evaporation loss |
NF T 60 101 CEC L-40 A-93 ASTM D5800 |
<0.6 |
% of mass |
|
Elastomer swelling 70h at 212°F |
ASTM D 4289.83 |
<0.5 |
Dimensional variation % |
|
Static temperature ranges Continuous Peak |
- - |
-20 +1200 -20 +1300 |
°C °C |
|
Rotation factor |
n.dm |
80,000 |
mm/min-1 |
|
4-ball test Wear scar diameter Wear load index |
ASTM D 2266 / ISO 20 623 |
0.50 4,800 |
mm daN |
|
TIMKEN Test |
ASTM D 2509 |
45 |
lbs |
|
EMCOR rust-prevention test Dynamic Static |
NF T 60 135 ISO DP 6294/ ASTM D 1743 |
1 1 |
Rating Rating |
|
Resistance to water washout at 80°C |
ASTM 1264 |
<2 |
% of mass |
|
ADDITIONAL PROPERTIES |
|||
|
PROPERTIES |
STANDARD OR METHOD |
VALUE |
UNIT |
|
Tightening torque at 20°C |
MIL A 907 E 80 |
80 |
Newton metres |
|
Loosening torque at 450°C |
MIL A 907 E 80 |
90 |
Newton metres |
|
Loosening torque at 750°C |
MIL A 907 E 80 |
100 |
Newton metres |
* not measured or non-measurable
PRESENTATION
|
|
Aerosol 650 ml |
Looking for another product?
|
Discover our entire range by clicking on the photo |
Manufacturing, lubrification, cleansing, protection,
IBiotec® Tec Industries® Service
offers a wide range of products reserved for industrial area
If you wish for :
a free sample
a technical advice
a product data sheet
a safety data sheet
IBiotec® Tec Industries®Service
manufacturer of technical chemical products.
Welcome to our website.
IBiotec® Tec Industries®Service is on : 